MECHANICAL ALLOYING OF FeCoCr

Gema González, Dariusk Oleszak, Amaya Sagarzazu, Rafael Villalba, Lisseta D’Onofrio

Online: 15-11-2010

GA-133

Abstract


The mechanical alloying of Fe-Co-Cr has been studied from the structural point of view by different techniques: XRD, TEM and Mössbauer spectroscopy, following the transformations taking place during milling. The alloys FeCo, Fe40Co50Cr10 and Fe50Co40Cr10 were prepared by milling of the elemental powders during 1, 2, 5, 10, 20, 40 and 60 h. The kinetics of alloy formation occurs by incorporation of Co and/or Cr in the Fe structure. For the Fe-Co alloy after 10h of milling a mixture of Fe (Co) solid solution and a-Fe is obtained. For the FeCoCr alloys prolonged milling results in Cr incorporation in the FeCo structure and a mixture of Fe (Co) and Fe (Cr) is formed. A grain size in the range of 2-5 nm is reached after 60h of milling.

El proceso de aleación mecánica de Fe-Co-Cr ha sido estudiado desde el punto de vista estructural por varias técnicas: DRX, MET, Espectroscopía Mössbauer, siguiendo las transformaciones que tienen lugar durante la molienda. Las aleaciones FeCo, Fe40Co50Cr10 y Fe50Co40Cr10 fueron preparadas a partir de los polvos elementales por molienda durante 1, 2, 5, 10, 20, 40 y 60 h. La cinética de formación de aleación ocurre por incorporación del Co y/o Cr en la estructura del Fe. Para la aleación Fe-Co después de 10 h de molienda se obtiene la mezcla de una solución sólida Fe (Co) y a-Fe. Para las aleaciones FeCoCr, la molienda prolongada resulta en la incorporación de Cr en la estructura de FeCo formándose una mezcla de Fe (Co) y Fe (Cr). Un tamaño de grano en el orden de 2-5 nm es obtenido después de 60 h de molienda.


PDFPDF (1MB)

Abstract Accessed: 1208 times

Article Downloaded: 1869 times


Cite: citation