PHOTOCATALYTIC PROPERTIES EVALUATION OF PORTLAND WHITE CEMENT ADDED WITH TiO2-NANOPARTICLES
(EVALUACIÓN DE LAS PROPIEDADES FOTOCATALÍTICAS DE CEMENTO PÓRTLAND BLANCO ADICIONADO CON NANOPARTÍCULAS DE DIÓXIDO DE TITANIO)

Carolina Cárdenas Ramírez, Jorge Iván Tobón, Claudia Patricia García García

Online: 12-11-2012

GA-301

Abstract


Photocatalytic activity of white Portland cement paste samples, added with 0.5, 1.0 and 3.0% wt of titanium dioxide nanoparticles, was evaluated trough the degradation of Rhodamine B. The degradation was measured by the change of the color coordinates CIE L*a*b* of samples exposed to a UV source and a photocatalytic efficiency coefficient, ξ, was calculated for two times of curing (65h and 28d). Three ratios of anatase:rutile were used (100:0, 85:15, 50,50) for each percentage of addition. Results showed that samples with the highest photocatalytic activity correspond to 3.0% of anatase at early ages, and 3.0% of anatase:rutile (50:50) at late ages.

La actividad fotocatalítica de pastas de cemento Pórtland blanco, adicionadas con 0,5%, 1,0% y 3,0% en peso de nanopartículas de dióxido de titanio, fue evaluada a través de la degradación de Rodamina B. La degradación fue medida en función del cambio en las coordenadas de color CIE L*a*b* de las muestras expuestas a un fuente ultravioleta, UV, y un coeficiente fotocatalítico, ξ, fue calculado para dos edades de curado (65 horas y 28 días). Tres proporciones de anatasa:rutilo fueron empleadas (100:0, 85:15, 50:50) para cada porcentaje de adición. Los resultados mostraron que las muestras con la mayor actividad fotocatalítica correspondieron a un 3,0% de anatasa a edades tempranas y un 3,0% de anatasa:rutilo (50:50) a edades tardías.