Rev. LatinAm. Metal. Mat. 2015, 35(2): 254-258

EXCHANGE-BIASED Fe4.6Co70.4Si15B10/NiO BILAYERS
(BICAPAS Fe4.6Co70.4Si15B10/NiO CON POLARIZACIÓN DE INTERCAMBIO)

Jose Rafael Fermin

Online: 06-02-2015

GA-625

Abstract


We report on experimental evidence of exchange bias between the amorphous ferromagnetic (FM) Fe4.6Co70.4Si15B10 and an antiferromagnetic (AF) NiO film, grown onto single crystalline Si(001) wafers. Surface Magneto-optic Kerr Effect (SMOKE) has been used to measure the hysteresis loop shift, and coercivity, as functions of the azimuthal angle, jH, and the FM layer thickness, t. The measurements reveal the presence of induced unidirectional and uniaxial symmetries following a complex cosine dependence, and thickness dependence proportional to 1/t, typical of interfacial effects.

Reportamos evidencia experimental de polarización de intercambio entre una película ferromagnética (FM) de Fe4.6Co70.4Si15B10 y una de NiO antiferromagnética (AF), depositadas sobre substratos de Si(001). Se obtuvieron las curvas de histéresis utilizando la técnica de Efecto Kerr Magnetoóptico de Superficie (SMOKE), y medimos el desplazamiento de las curvas y el campo coercitivo en función del ángulo acimutal, H, y el espesor de la película FM, t. Las medidas revelan la presencia de anisotropías unidireccional y uniaxial, cuyas asimetrías corresponden a funciones complejas de cos(H), y dependencia con el espesor proporcional a 1/t, típica de los efectos de interface.


PDFPDF (279KB)

Abstract Accessed: 887 times

Article Downloaded: 413 times


Cite: citation