SYNTHESIS, CRYSTAL STRUCTURE AND MAGNETIC BEHAVIOR OF C­uCo<sub>2</sub>InTe<sub>4</sub> AND CuNi<sub>2</sub>InTe<sub>4</sub><br>(<em>SÍNTESIS, ESTRUCTURA CRISTALINA Y COMPORTAMIENTO MAGNÉTICO DE CuCo<SUB>2</SUB>InTe<SUB>4</SUB> Y CuNi<SUB>2</SUB>InTe<SUB>4</SUB></em>)

Autores/as

  • Pedro Grima Gallardo Departamento de Física, Facultad de Ciencias, Universidad de Los Andes
  • Miguel Soto
  • Orlando Izarra
  • Luis Nieves
  • Miguel Quintero
  • Gerzon E. Delgado
  • Humberto Cabrera
  • Inti Zumeta-Dubé
  • Alejandro Rodríguez
  • Jennifer R Glenn
  • Jennifer A. Aitken

Resumen

Polycrystalline samples of nominal CuCo2InTe4 and CuNi2InTe4 were prepared by the melt and anneal method and the products characterized by powder X-ray diffraction and SQUID techniques. It was found that CuCo2InTe4 and CuNi2InTe4 crystallize in the tetragonal space group (Nº 121), Z = 2, in a stannite-type structure, with the binaries CoTe and NiTe as secondary phases, respectively. The magnetic behavior of CuCo2InTe4 is that of a superparamagnetic state with an irreversibility temperature of ~450K and a maximum coercive field of 35 Oe at 2K; whereas CuNi2InTe4 shows two magnetic components, one diamagnetic an another weak ferromagnetic. Se prepararon muestras policristalinas de CuCo2InTe4 and CuNi2InTe4 en su valor nominal por el método de fusión y recocido, y los productos fueron caracterizados por las técnicas de difracción de rayos X y SQUID. Se encontró que CuCo2InTe4 and CuNi2InTe4 cristalizan en una estructura tetragonal, grupo espacial (Nº 121), Z = 2, tipo estannita, con presencia de los binarios CoTe y NiTe como fases secundarias, respectivamente. El comportamiento magnético de CuCo2InTe4 es de tipo superparamagnético con una temperatura de irreversibilidad de ~450K y un campo coercitivo máximo de 35 Oe a 2K; mientras que CuNi2InTe4 presenta dos componentes magnéticas, una diamagnética y otra ferromagnética débil.

Descargas

Los datos de descargas todavía no están disponibles.

Descargas

Publicado

2016-10-04

Cómo citar

Grima Gallardo, P., Soto, M., Izarra, O., Nieves, L., Quintero, M., Delgado, G. E., Cabrera, H., Zumeta-Dubé, I., Rodríguez, A., Glenn, J. R., & Aitken, J. A. (2016). SYNTHESIS, CRYSTAL STRUCTURE AND MAGNETIC BEHAVIOR OF C­uCo&lt;sub&gt;2&lt;/sub&gt;InTe&lt;sub&gt;4&lt;/sub&gt; AND CuNi&lt;sub&gt;2&lt;/sub&gt;InTe&lt;sub&gt;4&lt;/sub&gt;&lt;br&gt;(&lt;em&gt;SÍNTESIS, ESTRUCTURA CRISTALINA Y COMPORTAMIENTO MAGNÉTICO DE CuCo&lt;SUB&gt;2&lt;/SUB&gt;InTe&lt;SUB&gt;4&lt;/SUB&gt; Y CuNi&lt;SUB&gt;2&lt;/SUB&gt;InTe&lt;SUB&gt;4&lt;/SUB&gt;&lt;/em&gt;). Revista Latinoamericana De Metalurgia Y Materiales, 83–92. Recuperado a partir de https://www.rlmm.org/ojs/index.php/rlmm/article/view/761

Número

2017, 37(1)

Sección

Artí­culos Regulares

Licencia

Los autores de Artículos Aceptados para su publicación por parte de la RLMM, deberán reconocer la completa transferencia de los derechos de autor en todos los idiomas a la RLMM. Esta transferencia incluye el derecho de la RLMM de adaptar el Artículo para fines de reproducción en medios digitales o impresos sin alterar su contenido escrito así como la información mostrada en tablas o figuras que hayan sido aceptadas para su publicación.
Los autores conservan los derechos de autor y garantizan a la revista el derecho de ser la primera publicación del trabajo al igual que licenciado bajo una Creative Commons Attribution License 4.0 Internacional (CC BY 4.0) que permite a otros compartir el trabajo con un reconocimiento de la autoría del trabajo y la publicación inicial en esta revista.